核电涂层性能测试标准为ASTM标准，主要对于核电涂料的热传导率、盐雾耐腐蚀性，耐辐照性能，防火性能，附着力，耐高温试验以及耐人工老化试验等。其中核电涂料热传导率测试根据ASTM E1461及ASTM E1530，要求核电涂料ASTM E1461及ASTM E1530热传导率指标≥0.6W/m.K (或者0.4-0.7)。南京睿督公司专业提供涂料ASTM E1461及ASTM E1530热导测试，具体内容请咨询南京睿督公司，咨询电话：025-8658 3475。

核电涂料热导率测试标准ASTM E1461及ASTM E1530，国内众多厂家的核电涂料ASTM E1530热导测试报告，均由我司提供，拥有丰富的实际测试经验。

ASTM E1461热导测试闪光法：
ASTM E1461 Standard test method for thermal diffusivity by the flash method.
ASTM E1461 闪光法测定热扩散系数的标准方法
 
ASTM E1461标准适用范围：
ASTM E1461标准用于确定各项同性固体材料的热扩散系数，用本方法可以很容易测试从75K到2800K热扩散系数在10-7到10-3的材料。
This test method covers the determination of the thermal diffusivity of primarily homogeneous isotropic solid materials. Thermal diffusivity values ranging from 10-7 to 10-3 m2/s are readily measurable by this test method from about 75 to 2800K.
 
ASTM E1461标准术语：
固体材料的热导率λ-稳定热流通过均质材料的无限平板的垂直于表面方向的单位厚度，引起单位温差的热流速率。由于其随温度的变化是变化的，该性质定义时需说明是某一特定的平均温度下的值。
固体材料热扩散系数α-其由热导率除以密度和单位质量热容的乘积得到。
 
ASTM E1461：用闪光法（激光闪射法）确定固体热扩散率的试验方法，高强度的能量脉冲对小而薄的圆盘试样进行短时间的辐照。脉冲的能量被样品的前表面吸收并记录其所导致后表面温度上升（温度自记曲线）。热扩散系数的值通过试样的厚度和后表面温度上升达到某一比值的最大值所需要的时间计算出来。原理是一束激光打在样品上表面，用红外检测器测下表面的温度变化，实际测得的数据是样品的热扩散率。

涂料导热系数测试标准-ASTM E1530/ ASTM E 1530-19
ASTM E1530 Standard Test Method for Evaluating the Resistance to Thermal Transmission of Materials by the Guarded Heat Flow Meter Technique。
ASTM E 1530用保护的热流计技术评定材料的耐传热性能的测试标准。

涂料导热系数测试方法-ASTM E1530/ ASTM E 1530-19
This test method covers a steady-state technique for the determination of the resistance to thermal transmission (thermal resistance) of materials in thickness of less than 25mm. This test method is useful for materials having a thermal resistance in the range from 10 to 400 ×10-4 m2 k/w thermal conductivity in the approximate range, temperature range from 150 to 400K. It can be used outside these ranges with reduced accuracy for thicker specimens and for thermal conductivity values up to 60W/(M.K)

ASTM E1530导热系数-样品要求
ASTM E1530样品要求：The recommended specimen configuration is a 50.8±0.25mm diameter disk, having smooth flat and parallel faces. The thickness less than 25mm.
导热系数与材料的组成结构、密度、含水率、温度等因素有关。非晶体结构、密度较低的材料，导热系数较小。材料的含水率、温度较低时，导热系数较小。

涂料ASTM E1530及ASTM E1461热导测试相关资料
ASTM E408发射率测试 http://www.fire-test.com/teststandard/usa/7147.html
ASTM E1980反射系数SRI测试 http://www.fire-test.com/teststandard/usa/7148.html
ASTM E1530热导测试 http://www.firete.com/popular_standards/9760.html 
ASTM E1530 / ASTM D 5470 http://www.firete.com/popular_standards/9764.html

南京睿督公司已成功协助国内多家大型涂料油漆的厂家，成功取得美标ASTM E1530及ASTM E1461热导检测报告，具体请咨询南京睿督公司

南京睿督公司全国免费咨询电话：400-603-6575   025-8658 3475
网址：www.fire-test.com    