ASTM D5229/D5229M 聚合物基复合材料水分吸收性能和平衡条件的标准试验方法
ASTM D5229/D5229M Standard Test Method for Moisture Absorption Properties and Equilibrium Conditioning of Polymer Matrix Composite Materials

Moisture Absorption of Matrix Composites by ASTM D5229
SMART tests matrix composite materials for moisture absorption, using ASTM D5229.

Moisture absorption of matrix composites ASTM D5229 scope:
Moisture Absorption of Matrix Composites (ASTM D5229) is a gravimetric test method that monitors change over time of moisture content by measuring the total mass change of a coupon that is exposed to a specified environment. Within ASTM D5229 there are three other procedures covering material conditioning within a specific moisture environment.

Test procedure:
For Procedure A, at least five 100 mm * 100 mm test specimens are machined from customer supplied product. The side edges are then sealed to prevent moisture absorption through the sides. The specimens are then dried, removed from the drying oven, and allowed to cool in a desiccator. The specimens are then weighed on an analytical balance to the nearest 0.1 mg. The specimens are then placed in the appropriate conditioning environment. The specimens are removed from the conditioning environment periodically, allowed to equilibrate to room temperature in a sealed container, and weighed. This procedure is repeated until there is no discernable increase in specimen weight.

Specimen size:
A common size is 100 mm * 100 mm.

Data:
Calculated mass change at equilibrium: Mass Change = (Wi – Wb) / Wb * 100

南京睿督公司咨询电话:025-8658 3475    400-603-6575
网址:www.fire-test.com    www.fire-test.cn
Email:info@hksmartps.com 

……

地址:江苏省南京市建邺区江东中路118号德盈大厦1622
电话:025-8658 3475
传真:025-8658 3457
网址:http://www.bs6853.com/
邮箱:info@fire-test.com

脚注信息
版权所有 Copyright(C)2012-2015  南京睿督科技有限公司 版权所有  苏公网安备 32010502010099号    备案号:苏ICP备10201999号-9
图片